An experimental program was implemented where wall panels were obtained from two existing vintage unreinforced clay brick masonry (URM) buildings and subjected to a diagonal compression loading condition in order to induce a diagonal tension failure mode. The principal aims of the experimental program were to establish the diagonal tension strength of the vintage clay brick URM walls present in the two buildings and to establish a benchmark mortar mix suitable for use when manufacturing replica clay brick test assemblages that adequately represent the strength characteristics present in vintage URM buildings. It was concluded that the use of recycled clay bricks acquired from vintage URM buildings and a mortar mix of 1:2:9 (cement:lime:sand) appropriately replicates the material strength characteristics that are present in existing vintage clay brick URM buildings located in New Zealand AM - Accepted Manuscript
The large number of earthquake-prone vintage unreinforced masonry (URM) buildings in many seismically active parts of the world results in a need for minimally invasive and cost-effective strengthening techniques to enhance the poor earthquake performance of such buildings. The objective of the research reported here was to investigate the applicability of using near-surface-mounted (NSM) carbon fiber–reinforced polymer (CFRP) strips as a retrofitting technique for improving the in-plane shear strength and displacement capacity of multi-leaf URM walls constructed using solid clay brick masonry. The use of this technique for repairing earthquake damaged URM walls was also investigated. Ten multileaf wall panels measuring approximately 1,200×1,200 mm 1,200×1,200 mm were constructed using recycled vintage solid clay bricks and retrofitted using NSM CFRP strips with varying reinforcement ratios. These panels were loaded in diagonal compression, and the results were compared with those obtained from testing of nominally identical unretrofitted wall panels constructed using the same materials. In addition, four wall panels extracted from existing buildings were tested in an as-built condition and then later retested after being repaired using the NSM CFRP strip technique. Based on the experimental results it was established that the NSM CFRP strip technique provides a simple and cost effective method for substantially enhancing the shear strength and displacement capacity of understrength or damaged URM wall panels http://ascelibrary.org/journal/jccof2
New Zealand's devastating Canterbury earthquakes provided an opportunity to examine the efficacy of existing regulations and policies relevant to seismic strengthening of vulnerable buildings. The mixed-methods approach adopted, comprising both qualitative and quantitative approaches, revealed that some of the provisions in these regulations pose as constraints to appropriate strengthening of earthquake-prone buildings. Those provisions include the current seismic design philosophy, lack of mandatory disclosure of seismic risks and ineffective timeframes for strengthening vulnerable buildings. Recommendations arising from these research findings and implications for pre-disaster mitigation for future earthquake and Canterbury's post-disaster reconstruction suggest: (1) a reappraisal of the requirements for earthquake engineering design and construction, (2) a review and realignment of all regulatory frameworks relevant to earthquake risk mitigation, and (3) the need to develop a national programme necessary to achieve consistent mitigation efforts across the country. These recommendations are important in order to present a robust framework where New Zealand communities such as Christchurch can gradually recover after a major earthquake disaster, while planning for pre-disaster mitigation against future earthquakes AM - Accepted Manuscript
The collapse of Redcliffs’ cliff in the 22 February 2011 and 13 June 2011 earthquakes were the first times ever a major failure incident occurred at Redcliffs in approximately 6000 years. This master’s thesis is a multidisciplinary engineering geological investigation sought to study these particular failure incidents, focusing on collecting the data necessary to explain the cause and effect of the cliff collapsing in the event of two major earthquakes. This study provides quantitative and qualitative data about the geotechnical attributes and engineering geological nature of the sea-cut cliff located at Redcliffs. Results from surveying the geology of Redcliffs show that the exposed lithology of the cliff face is a variably jointed rock body of welded and (relatively intact) unwelded ignimbrite, a predominantly massive unit of brecciated tuff, and a covering of wind-blown loess and soil deposit (commonly found throughout Canterbury) on top of the cliff. Moreover, detailing the external component of the slope profile shows that Redcliffs’ cliff is a 40 – 80 m cliff with two intersecting (NE and SE facing) slope aspects. The (remotely) measured geometry of the cliff face comprises of multiple outstanding gradients, averaging a slope angle of ~67 degrees (post-13 June 2011), where the steepest components are ~80 degrees, whereas the gentle sloping sections are ~44 degrees. The physical structure of Redcliffs’ cliff drastically changed after each collapse, whereby seismically induced alterations to the slope geometry resulted in material deposited on the talus at the base of the cliff. Prior to the first collapse, the variance of the gradient down the slope was minimal, with the SE Face being the most variable with up to three major gradients on one cross section. However, after each major collapse, the variability increased with more parts of the cliff face having more than one major gradient that is steeper or gentler than the remainder of the slope. The estimated volume of material lost as a result of the gradient changes was 28,267 m³ in February and 11,360 m³ in June 2011. In addition, surveys of the cliff top after the failure incidents revealed the development of fissures along the cliff edge. Monitoring 10 fissures over three months indicated that fissured by the cliff edge respond to intense seismicity (generally ≥ Mw 4) by widening. Redcliffs’ cliff collapsed on two separate occasions as a result of an accumulated amount of damage of the rock masses in the cliff (caused by weathering and erosion over time), and two Mw 6.2 trigger earthquakes which shook the Redcliffs and the surrounding area at a Peak Ground Acceleration (PGA) estimated to be around 2 g. The results of the theoretical study suggests that PGA levels felt on-site during both instances of failure are the result of three major factors: source of the quake and the site affected; topographic amplification of the ground movement; the short distance between the source and the cliff for both fault ruptures; the focus of seismic energy in the direction of thrust faulting along a path that intercepts Redcliffs (and the Port Hills). Ultimately, failure on the NE and SE Faces of Redcliffs’ cliff was concluded to be global as every part of the exposed cliff face deposited a significant volume of material on the talus at the base of the cliff, with the exception of one section on the NE Face. The cliff collapses was a concurrent process that is a single (non-monotonic) event that operated as a complex series of (primarily) toppling rock falls, some sliding of blocks, and slumping of the soil mantle on top of the cliff. The first collapse had a mixture of equivalent continua slope movement of the heavily weathered / damaged surface of the cliff face, and discontinuous slope movement of the jointed inner slope (behind the heavily weathered surface); whereas the second collapse resulted in only discontinuous slope movement on account of the freshly exposed cliff face that had damage to the rock masses, in the form of old and (relatively) new discontinuous fractures, induced by earthquakes and aftershocks leading up to the point of failure.