An experimental program was implemented where wall panels were obtained from two existing vintage unreinforced clay brick masonry (URM) buildings and subjected to a diagonal compression loading condition in order to induce a diagonal tension failure mode. The principal aims of the experimental program were to establish the diagonal tension strength of the vintage clay brick URM walls present in the two buildings and to establish a benchmark mortar mix suitable for use when manufacturing replica clay brick test assemblages that adequately represent the strength characteristics present in vintage URM buildings. It was concluded that the use of recycled clay bricks acquired from vintage URM buildings and a mortar mix of 1:2:9 (cement:lime:sand) appropriately replicates the material strength characteristics that are present in existing vintage clay brick URM buildings located in New Zealand AM - Accepted Manuscript
New Zealand’s stock of unreinforced masonry (URM) bearing wall buildings was principally constructed between 1880 and 1935, using fired clay bricks and lime or cement mortar. These buildings are particularly vulnerable to horizontal loadings such as those induced by seismic accelerations, due to a lack of tensile force-resisting elements in their construction. The poor seismic performance of URM buildings was recently demonstrated in the 2011 Christchurch earthquake, where a large number of URM buildings suffered irreparable damage and resulted in a significant number of fatalities and casualties. One of the predominant failure modes that occurs in URM buildings is diagonal shear cracking of masonry piers. This diagonal cracking is caused by earthquake loading orientated parallel to the wall surface and typically generates an “X” shaped crack pattern due to the reversed cyclic nature of earthquake accelerations. Engineered Cementitious Composite (ECC) is a class of fiber reinforced cement composite that exhibits a strain-hardening characteristic when loaded in tension. The tensile characteristics of ECC make it an ideal material for seismic strengthening of clay brick unreinforced masonry walls. Testing was conducted on 25 clay brick URM wallettes to investigate the increase in shear strength for a range of ECC thicknesses applied to the masonry wallettes as externally bonded shotcrete reinforcement. The results indicated that there is a diminishing return between thickness of the applied ECC overlay and the shear strength increase obtained. It was also shown that, the effectiveness of the externally bonded reinforcement remained constant for one and two leaf wallettes, but decreased rapidly for wall thicknesses greater than two leafs. The average pseudo-ductility of the strengthened wallettes was equal to 220% of that of the as-built wallettes, demonstrating that ECC shotcrete is effective at enhancing both the in-plane strength and the pseudo-ductility of URM wallettes AM - Accepted Manuscript
The large number of earthquake-prone vintage unreinforced masonry (URM) buildings in many seismically active parts of the world results in a need for minimally invasive and cost-effective strengthening techniques to enhance the poor earthquake performance of such buildings. The objective of the research reported here was to investigate the applicability of using near-surface-mounted (NSM) carbon fiber–reinforced polymer (CFRP) strips as a retrofitting technique for improving the in-plane shear strength and displacement capacity of multi-leaf URM walls constructed using solid clay brick masonry. The use of this technique for repairing earthquake damaged URM walls was also investigated. Ten multileaf wall panels measuring approximately 1,200×1,200 mm 1,200×1,200 mm were constructed using recycled vintage solid clay bricks and retrofitted using NSM CFRP strips with varying reinforcement ratios. These panels were loaded in diagonal compression, and the results were compared with those obtained from testing of nominally identical unretrofitted wall panels constructed using the same materials. In addition, four wall panels extracted from existing buildings were tested in an as-built condition and then later retested after being repaired using the NSM CFRP strip technique. Based on the experimental results it was established that the NSM CFRP strip technique provides a simple and cost effective method for substantially enhancing the shear strength and displacement capacity of understrength or damaged URM wall panels http://ascelibrary.org/journal/jccof2
High demolition rates were observed in New Zealand after the 2010-2011 Canterbury Earthquake Sequence despite the success of modern seismic design standards to achieve required performance objectives such as life safety and collapse prevention. Approximately 60% of the multi-storey reinforced concrete (RC) buildings in the Christchurch Central Business District were demolished after these earthquakes, even when only minor structural damage was present. Several factors influenced the decision of demolition instead of repair, one of them being the uncertainty of the seismic capacity of a damaged structure. To provide more insight into this topic, the investigation conducted in this thesis evaluated the residual capacity of moderately damaged RC walls and the effectiveness of repair techniques to restore the seismic performance of heavily damaged RC walls. The research outcome provided insights for developing guidelines for post-earthquake assessment of earthquake-damaged RC structures. The methodology used to conduct the investigation was through an experimental program divided into two phases. During the first phase, two walls were subjected to different types of pre-cyclic loading to represent the damaged condition from a prior earthquake, and a third wall represented a repair scenario with the damaged wall being repaired using epoxy injection and repair mortar after the pre-cyclic loading. Comparisons of these test walls to a control undamaged wall identified significant reductions in the stiffness of the damaged walls and a partial recovery in the wall stiffness achieved following epoxy injection. Visual damage that included distributed horizontal and diagonal cracks and spalling of the cover concrete did not affect the residual strength or displacement capacity of the walls. However, evidence of buckling of the longitudinal reinforcement during the pre-cyclic loading resulted in a slight reduction in strength recovery and a significant reduction in the displacement capacity of the damaged walls. Additional experimental programs from the literature were used to provide recommendations for modelling the response of moderately damaged RC walls and to identify a threshold that represented a potential reduction in the residual strength and displacement capacity of damaged RC walls in future earthquakes. The second phase of the experimental program conducted in this thesis addressed the replacement of concrete and reinforcing steel as repair techniques for heavily damaged RC walls. Two walls were repaired by replacing the damaged concrete and using welded connections to connect new reinforcing bars with existing bars. Different locations of the welded connections were investigated in the repaired walls to study the impact of these discontinuities at the critical section. No significant changes were observed in the stiffness, strength, and displacement capacity of the repaired walls compared to the benchmark undamaged wall. Differences in the local behaviour at the critical section were observed in one of the walls but did not impact the global response. The results of these two repaired walls were combined with other experimental programs found in the literature to assemble a database of repaired RC walls. Qualitative and quantitative analyses identified trends across various parameters, including wall types, damage before repair, and repair techniques implemented. The primary outcome of the database analysis was recommendations for concrete and reinforcing steel replacement to restore the strength and displacement capacity of heavily damaged RC walls
